11 Years Factory SV-999 Structural Glazing Silicone Sealant Supply to Georgia
Short Description:
Description SV – 999 silicone structural sealant is a one-component, neutral curing, designed for glass curtain wall, aluminum curtain wall, glass daylighting roof and metal structural engineering structural assembly silicone sealant. Show the effective physical properties and bonding performance Key Features 1. 100% silicone 2. No sag 3. Strong bonding strength 4. Water & weatherproof 5. Primerless adhesion to most building materials 6. 25% movement capability Basic Application...
Reliable quality and good credit standing are our principles, which will help us at a top-ranking position. Adhering to the tenet of "quality first, customer supreme" for 11 Years Factory SV-999 Structural Glazing Silicone Sealant Supply to Georgia, Sincerely hope we are growing up together with our customers all over the world.
Description
SV – 999 silicone structural sealant is a one-component, neutral curing, designed for glass curtain wall, aluminum curtain wall, glass daylighting roof and metal structural engineering structural assembly silicone sealant. Show the effective physical properties and bonding performance
Key Features
1. 100% silicone
2. No sag
3. Strong bonding strength
4. Water & weatherproof
5. Primerless adhesion to most building materials
6. 25% movement capability
Basic Application
1.Glass curtain wall, aluminum curtain wall structure adhesive seal
2.Glass daylighting roof, metal structure engineering
3.Insulating glass bonding
Technical data sheet
| Test standard | Test project | Unit | value |
| Before curing——25℃，50%R.H. | |||
| specific gravity | g/ml | 1.40 | |
| GB13477 | Flow, sagging or vertical flow | mm | 0 |
| GB13477 | Operating time | min | 15 |
| GB13477 | surface drying time（25℃，50%R.H.） | min | 40-60 |
| Sealant curing speed and operating time will have different with different temperatures and temperature, high temperature and high humidity can make sealant curing speed faster, rather low temperature and low humidity are slower.21 days after curing——25℃，50%R.H. | |||
| GB13477 | Durometer Hardness | Shore A | 40 |
| The ultimate tensile strength | Mpa | 1.3 | |
| GB13477 | Tensile strength（23℃） | Mpa | 0.8 |
| GB13477 | Tensile strength（90℃） | Mpa | 0.5 |
| GB13477 | Tensile strength（-30℃） | Mpa | 0.9 |
| GB13477 | Tensile strength（flooding） | Mpa | 0.6 |
| GB13477 | Tensile strength（flooding – ultraviolet） | Mpa | 0.6 |
Certification
GB 16776；ASTM C1184
Color
Black
Package
300ml in cartridge * 24 per box, 500ml in sausage *20 per box
Shelf life
12 months
Note
If you want the TDS or MSDS or other details, please contact with our sales person.
The surface of the automobile turns superhydrophobic after ~10 min of total flame treatment. The treated automobile exhibits high
water repellency, self-cleaning, and retains water repellency even after dumping 0.5 tons of water over the surface. The surface was rubbed with steel wool to wear the surface until loss
of water repellency. Water repellency was recovered by reprocessing with flame. Work published in Advanced Materials Volume 28, Issue 19, pages 3677–3682, May 18, 2016
BUY ArtResin here https://www.artresin.com/
Coating a bar top that had big knots in it! Embedded a coin in there. Shiny, hard and stands up to any weather.
We worked in 3 layers
1) fist coat was to let the resin soak into the wood and fill up some of the cracks.
2) second coat filled up all the remaining cracks and divets so they are level with the top surface.
3) a final top coat was applied to finish the whole thing!
www.artresin.com