Wholesale 100% Original SV-8890 Two-component Silicone Structural Glazing Sealant Export to Ghana
Short Description:
Description SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine constructi...
Our commission is to serve our users and clients with best quality and competitive portable digital products for Wholesale 100% Original SV-8890 Two-component Silicone Structural Glazing Sealant Export to Ghana, We sincerely look forward to hearing from you. Give us a chance to show you our professionalism and passion.
Description
SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine construction, two kinds of components in accordance with the provisions, mixing ratio after curing form elastomer.
Key Features
1. None sag
2. Adjustable working time
3. Excellent adhesion to most building substrates
4. High bonding strength and modulus
5.12.5%movement capability
6. Silicone durability
Basic Application
1.Glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal;
2.Insulating Glass of the second seal
3.Many other building and industrial applications
Technical data sheet
| Test project | Unit | value |
| Flow, sagging or vertical flow | mm | 0 |
| Operating time | min | 20 |
| surface drying time（25℃，50%R.H.） | min | 40-60 |
| Durometer Hardness | Shore A | 20-60 |
| At 23 ℃ maximum tensile strength elongation | % | ≥100 |
| Tensile strength（23℃） | Mpa | 0.9 |
| Tensile strength（90℃） | Mpa | 0.68 |
| Tensile strength（-30℃） | Mpa | 0.68 |
| Tensile strength（flooding） | Mpa | 0.68 |
| Tensile strength（flooding – ultraviolet） | Mpa | 0.68 |
| Bond damage area | % | 5 |
| Thermal aging（thermal weight loss） | % | ≤5 |
| Thermal aging（crack） | No | |
| Thermal aging（efflorescence） | No |
Certification
GB 16776
Color
Component A(Base) – White, Component B(Catalyst)- Black
Package
1. Component A(Base): (190L), Component B(Catalyst) (18.5L)
2. Component A(Base):24.5kg (18L), Component B(Catalyst): 1.9kg (1.8L)
Shelf life
12 months
Note
If you want the TDS or MSDS or other details, please contact with our sales person.
The coating Microsoft puts on the Mouse like the Wireless Intellimouse Explorer 2.0 seems to degrade and cause the black rubbery surface to become sticky. I’ve searched the internet and the only true solution to fixing this annoying problem is to sand the sticky residue from the black rubber coating. The mouse will look slightly scuffed on the black parts but at least it will never feel sticky again.
BTW: My mouse is only 1 year old before the problem started to happen.
Video sponsor: https://www.simplyadditions.com/
I had a small leak in my swimming pool and fixed it with ‘Fix-A-Leak. Here’s how to do it. You may have noticed that I had a chlorine tablet in the skimmer basket! Thanks to Richard Clark who has just posted “NEVER put tablets in the bottom of a skimmer basket. guaranteed pipe rot” I now know why the pipe was leaking, I had been doing that for some seven years!!! This no doubt also caused two of my pumps to fail.