factory customized SV-GT2000 High-speed rail subway silicone sealant Wholesale to Jamaica

factory customized SV-GT2000 High-speed rail subway silicone sealant Wholesale to Jamaica
  • factory customized SV-GT2000 High-speed rail subway silicone sealant Wholesale to Jamaicafactory customized SV-GT2000 High-speed rail subway silicone sealant Wholesale to Jamaica
  • factory customized SV-GT2000 High-speed rail subway silicone sealant Wholesale to Jamaicafactory customized SV-GT2000 High-speed rail subway silicone sealant Wholesale to Jamaica

Short Description:

Description SV-GT2000 High-speed rail subway silicone sealant is a one-component, low modulus, neutral curing adhesive. For most of the stone, ceramic and cement components, can produce excellent adhesion   Key Features (1) easy to use: can be used at any time out; (2) excellent thixotropy and extrusion, at any temperature (-40 ℃ to 100 ℃) can be extruded; (3) good adhesion, the stone, ceramics and cement components and other building materials with excellent adhesion properties; no poll...


Product Detail

Attentions

Application

Product Tags

Our company aims to operating faithfully, serving to all of our customers , and working in new technology and new machine constantly for factory customized SV-GT2000 High-speed rail subway silicone sealant Wholesale to Jamaica, Welcoming interested companies to cooperate with us, we look forward to having the opportunity of working with companies around the world for joint growth and mutual success.


Description

SV-GT2000 High-speed rail subway silicone sealant is a one-component, low modulus, neutral curing adhesive. For most of the stone, ceramic and cement components, can produce excellent adhesion

 

Key Features

(1) easy to use: can be used at any time out;

(2) excellent thixotropy and extrusion, at any temperature (-40 ℃ to 100 ℃) can be extruded;

(3) good adhesion, the stone, ceramics and cement components and other building materials with excellent adhesion properties; no pollution of the porous material;

(4) excellent weather resistance, aging performance, excellent tensile and compression resilience, can carry ± 30% displacement capacity;

(5) neutral curing, stone, cement and other building materials without corrosive, to overcome the shortcomings of acid corrosion material.

(6) base modulus: passive deformation occurs when the role of moderate stress on the concrete substrate to ensure that the concrete surface is not destroyed;

(7) high elasticity high recovery capacity: can be repeated from the seams with the movement, fast response fast response, permanent deformation of small.

 

Basic Application

1.For high-speed rail track, airport runway, highway irrigation joints sealed, can withstand large displacement;

2.Can also be used for other concrete pavement sealing, subway engineering, tunnels, bridges and other projects sealed.

 

Technical data sheet

Test project

Unit value
surface drying time(25℃,50%R.H.) min ≤60
Sagging(70℃) vertical mm ≤3
Horizontal mm 0
Mass loss rate / ≤5%
Elastic recovery rate / ≥80%
100% tensile strength 23℃ MPa ≤0.3
-20℃ MPa ≤0.3
tensile strength 23℃ MPa ≥1.0
-20℃ MPa ≤2.0
168 h after thermal aging (80 ℃) MPa ≥0.8
168 h after alkali treatment MPa ≥0.8
Breaking elongation 23℃ / ≥800%
-20℃ / ≥600%
168 h after thermal aging (80 ℃) / ≥600%
168 h after alkali treatment / ≥600%
Bond strength 23℃ / No damaging
-20℃ / No damaging
168 h after thermal aging (80 ℃) / No damaging
96 h after immersion / No damaging
         

 

 

Color

Black, White, Gray

 

Package

300ml in cartridge * 24 per box, 590ml in sausage *20 per box

 

Shelf life

12 months

 

Note

If you want the TDS or MSDS or other details, please contact with our sales person.

  • Previous:
  • Next:



  • How to Stop Infiltration into a Manhole



    https://www.raytech.it/

    Procedure: pour the two components of Ray RTV in equal quantity in a measuring cup and mix for 30″ max. Put the frame inside the box, pour the compound and wait few minutes for the complete crosslinking reaction. Use RayResin to create the frame. Remove the separator and mix the two components of the resin for 3-5 minutes. Pour the compound into the mould and wait for the complete crosslinking reaction.