operation guides to make a multiple pieces mold for large products



Description:
HY-635# plaster cast silicone is mainly used for plaster products molds with the advantages of high tear strength, high durability, high temperature resistance, long shelf life, high duplication times etc. It is suitable for small products or fine and precision products which is difficult to demould. This plaster molding silicone is one of the products with the highest use level in the production of many kinds of products, and the shrinkage is even lower than 2‰.The rtv mold making silicone rubber(condensation curing) is generally called two-component room temperature vulcanization type with excellent fluidity and operational performance. Add curing agent of 2%-3% at room temperature, the plaster molding silicone is still operational within 30 minutes,and in 2-5 hours, a high tear silicone elastomers will be obtained with resistance to deformation, high-temperature, acid and alkali, and expansion.

Applications:
This high tear strentgh silicone rubber can be used in making molds for plaster, polyurethane , lighting ornaments, model design, stationery gifts, artifacts replia, PU crafts, and so on.

Plaster Molding Silicone Standard Datasheet:
Model
Appearance
Viscosity  (cps)
Hardness (A°)
Tensile Strength (Mpa)
Tear Strength (KN/m)
Elongation (%)
Mixing ratio(%)
Operating Time(H)
Curing Time(H)
635
White
≤38000
36±2
≥3.8
≥28
≥360
2~3
0.5~1
2~5

Operation Instruction for rtv-2 plaster moulding material :
  Our product, a flowing liquid with general hardness of 34—38A°after curing process, is in white color. also you can add some dye according to your needs, but you should contact with us first, because some type of dye will affect the silicone property and quality. If customer wants to make large products and large size molds, the mold should be made of silicone rubber with high hardness. On the contrary, if the mold with fine and precision patterns , it should be made of silicone with low hardness. The amount of the curing agent depends on the actual requirements of the customer. If requires faster drying rate, more curing agent should be needed; contrarily, if requires slower drying, less curing agent is needed. If all the operation is correct, you will obtain a perfect silicone elastomers for molding. The operation is not difficult, our salesmen can give tailored molding scheme for customers.(every salesmen of Hong ye company is well trained to provide with related technical consultation)

The proportions and reactions of the curing agent and the silicone are listed as follows:
  1. Adding curing agent 1%, the silicone could still be operated within 2.5 hours, and could be demoulded after 6-8 hours.
  2. Adding curing agent 2%, the silicone could still be operated within 50 minutes to 1 hour and could be demoulded after 2-3 hours.
  3. Adding curing agent 3%, the silicone could still be operated within 28 – 30 minutes and could be demoulded after 1.5-2 hours.
  4. Adding curing agent 4%, the silicone could still be operated within 10 – 15 minutes and could be demoulded after 1 -1.5 hours.

Any more information abt liquid casting silicone for plaster figurines, pls feel free to contact Ms. Jojo:
Mobile: 0086-15013774669
Tel: 0086-755-89212380
Fax: 0086-755-89948030
Website: www. szrl.net
Email:hyxz@szrl.net
Skype: Jojo Zhou


Post time: Aug-05-2017
INQUIRY NOW
  • * CAPTCHA: Please select the Truck