Hot Selling for SV-8890 Two-component Silicone Structural Glazing Sealant to Romania Manufacturer
Short Description:
Description SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine constructi...
Sticking to the principle of "Super Quality, Satisfactory service" ,We are striving to be a good business partner of you for Hot Selling for SV-8890 Two-component Silicone Structural Glazing Sealant to Romania Manufacturer, We are always looking forward to forming successful business relationships with new clients around the world.
Description
SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine construction, two kinds of components in accordance with the provisions, mixing ratio after curing form elastomer.
Key Features
1. None sag
2. Adjustable working time
3. Excellent adhesion to most building substrates
4. High bonding strength and modulus
5.12.5%movement capability
6. Silicone durability
Basic Application
1.Glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal;
2.Insulating Glass of the second seal
3.Many other building and industrial applications
Technical data sheet
| Test project | Unit | value |
| Flow, sagging or vertical flow | mm | 0 |
| Operating time | min | 20 |
| surface drying time（25℃，50%R.H.） | min | 40-60 |
| Durometer Hardness | Shore A | 20-60 |
| At 23 ℃ maximum tensile strength elongation | % | ≥100 |
| Tensile strength（23℃） | Mpa | 0.9 |
| Tensile strength（90℃） | Mpa | 0.68 |
| Tensile strength（-30℃） | Mpa | 0.68 |
| Tensile strength（flooding） | Mpa | 0.68 |
| Tensile strength（flooding – ultraviolet） | Mpa | 0.68 |
| Bond damage area | % | 5 |
| Thermal aging（thermal weight loss） | % | ≤5 |
| Thermal aging（crack） | No | |
| Thermal aging（efflorescence） | No |
Certification
GB 16776
Color
Component A(Base) – White, Component B(Catalyst)- Black
Package
1. Component A(Base): (190L), Component B(Catalyst) (18.5L)
2. Component A(Base):24.5kg (18L), Component B(Catalyst): 1.9kg (1.8L)
Shelf life
12 months
Note
If you want the TDS or MSDS or other details, please contact with our sales person.
This is how I water-proof my watch straps and other leather products such as my belt, daily wearing shoes, and snow boots. It really works well and protects the leather from wear (scuffing just wipes away). This is for a Di-Modell alligator strap but I’ve used it on many other watch straps – but with Hirsch straps I’ve found that the inner core still gets smelly where the holes for the tang buckle are. The AERO lining of Di-Modell is really awesome and I’ve used a Rallye strap all summer with no smells at all. Also, Di-Modell’s seem to have rounded sides whereas many Hirsch are more square or 90 degrees, which tend to dig into my wrist after time.