2017 New Style SV-8890 Two-component Silicone Structural Glazing Sealant for Washington Factories
Short Description:
Description SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine constructi...
Our pursuit and company goal is to "Always satisfy our customer requirements". We continue to develop and design superior quality products for both our old and new customers and achieve a win-win prospect for our clients as well as us for 2017 New Style SV-8890 Two-component Silicone Structural Glazing Sealant for Washington Factories, With superb service and quality, and an enterprise of foreign trade featuring validity and competitiveness, that will be trusted and welcomed by its clients and creates happiness to its employees.
Description
SV8890 is neutral curing, designed for glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. When using, SV8890 with dedicated two-component glue machine construction, two kinds of components in accordance with the provisions, mixing ratio after curing form elastomer.
Key Features
1. None sag
2. Adjustable working time
3. Excellent adhesion to most building substrates
4. High bonding strength and modulus
5.12.5%movement capability
6. Silicone durability
Basic Application
1.Glass, stone, marble, granite, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal;
2.Insulating Glass of the second seal
3.Many other building and industrial applications
Technical data sheet
| Test project | Unit | value |
| Flow, sagging or vertical flow | mm | 0 |
| Operating time | min | 20 |
| surface drying time（25℃，50%R.H.） | min | 40-60 |
| Durometer Hardness | Shore A | 20-60 |
| At 23 ℃ maximum tensile strength elongation | % | ≥100 |
| Tensile strength（23℃） | Mpa | 0.9 |
| Tensile strength（90℃） | Mpa | 0.68 |
| Tensile strength（-30℃） | Mpa | 0.68 |
| Tensile strength（flooding） | Mpa | 0.68 |
| Tensile strength（flooding – ultraviolet） | Mpa | 0.68 |
| Bond damage area | % | 5 |
| Thermal aging（thermal weight loss） | % | ≤5 |
| Thermal aging（crack） | No | |
| Thermal aging（efflorescence） | No |
Certification
GB 16776
Color
Component A(Base) – White, Component B(Catalyst)- Black
Package
1. Component A(Base): (190L), Component B(Catalyst) (18.5L)
2. Component A(Base):24.5kg (18L), Component B(Catalyst): 1.9kg (1.8L)
Shelf life
12 months
Note
If you want the TDS or MSDS or other details, please contact with our sales person.
Upgrade your kitchen bakeware with these Silicone baking cups from Marson Products. No muffin pan or baking cups needed easy cleanup just bake clean and reuse muffins pop right out. Dishwasher safe on top rack or hand washing recommended to extend life of the product. These cupcake baking cups are safe to use in oven up to 500 degrees. Each set of 12 comes in assorted bright colors. Limited Lifetime warranty against defects.
Medical Murray at MD&M West 2013, Anaheim, CA https://www.mdmwest.com
https://www.medicalmurray.com
Accomplishing new minimally invasive procedures often requires the construction of complicated catheters to access different anatomies, deliver devices or drugs and incorporate sensors to assure proper results. This requires the combination of many materials to provide different flexibility, low friction, torsional resistance, multiple paths and functional components; all in small diameters. Materials commonly utilized to achieve the required results include Nitinol, polyurethane, high density polyethylene, stainless steel, silicone rubber, Pt-Ir, PTFE, conductive wires, etc. Techniques for assembling these complex catheters will be explained; to include braiding over multiple lumens, axial reinforcement, injection molded access ports integrated into the handles, silicone balloons bonded to polyurethane, release mechanisms and sensor integration.